How to Improve the Service Life of the Tundish Metering Nozzle
1. Introduction
The tundish metering nozzle (TMN), also referred to as the tundish nozzle or metering nozzle insert, is a critical functional refractory used in continuous casting operations. Installed at the bottom of the tundish, it controls molten steel flow into the submerged entry nozzle (SEN) or directly into the mold, depending on the casting configuration. The performance and service life of the tundish metering nozzle directly influence casting stability, steel cleanliness, sequence length, productivity, and operational safety.
In modern steelmaking, increasing casting speed, longer casting sequences, higher steel cleanliness requirements, and aggressive steel grades place increasingly severe demands on tundish metering nozzles. Premature failure caused by erosion, corrosion, clogging, thermal shock, or structural cracking can lead to flow instability, steel breakout, unplanned tundish changes, and significant economic losses.
Therefore, improving the service life of tundish metering nozzles is a key technical objective for steel plants and refractory suppliers alike. This article systematically analyzes failure mechanisms and provides practical, engineering-oriented strategies to extend tundish metering nozzle life from the perspectives of material selection, structural design, manufacturing process, steel chemistry control, tundish operation, and quality management.
2. Failure Mechanisms of Tundish Metering Nozzles
Understanding failure mechanisms is the foundation for life improvement.
2.1 Chemical Corrosion
Molten steel and slag aggressively attack nozzle materials, especially under high oxygen activity and high CaO–Al₂O₃ slag systems. Typical corrosion mechanisms include:
-
Dissolution of Al₂O₃ or ZrO₂ into slag
-
Chemical reaction between steel inclusions and refractory phases
-
Flux penetration into open pores and grain boundaries
High-Mn, high-Ti, ultra-low carbon (ULC), and calcium-treated steels exacerbate corrosion.
2.2 Erosion by Molten Steel Flow
High casting speed increases molten steel velocity at the nozzle bore, resulting in:
-
Mechanical erosion of the working surface
-
Enlargement of bore diameter
-
Loss of flow control accuracy
Localized turbulence and asymmetric flow further intensify wear.
2.3 Nozzle Clogging
Clogging is one of the most severe life-limiting factors and is mainly caused by:
-
Deposition of Al₂O₃ inclusions
-
Reaction between steel and nozzle material
-
Reoxidation products formed at steel–air interfaces
Clogging reduces effective bore diameter, disturbs flow, and often forces premature nozzle replacement.
2.4 Thermal Shock and Structural Cracking
Rapid temperature changes during preheating, start casting, ladle change, or emergency shutdown can induce:
-
Thermal stress cracking
-
Spalling
-
Interfacial delamination in composite nozzles
2.5 Mechanical Damage and Assembly Issues
Improper installation, misalignment, or excessive tightening can introduce mechanical stress, leading to early fracture or leakage.
3. Optimization of Raw Material Selection
3.1 High-Purity Zirconia-Based Materials
ZrO₂-based materials are widely used due to their excellent corrosion resistance and low wettability to molten steel.
Key optimization points include:
-
ZrO₂ content ≥ 75–90% in the working layer
-
Low impurity levels (SiO₂, Fe₂O₃ < 0.3%)
-
Controlled grain size distribution for dense packing
High-purity zirconia significantly improves resistance to slag corrosion and steel erosion.
3.2 Stabilized Zirconia Systems
Pure zirconia undergoes phase transformation, causing volume expansion and cracking. Stabilizers are essential.
Common stabilizers:
-
CaO-stabilized ZrO₂ (CSZ)
-
MgO-stabilized ZrO₂ (MSZ)
-
Y₂O₃-stabilized ZrO₂ (YSZ)
Optimized stabilizer content improves thermal shock resistance while maintaining corrosion resistance.
3.3 Composite Material Design
Multi-layer or composite structures are increasingly adopted:
-
ZrO₂-rich inner bore for corrosion and clogging resistance
-
Al₂O₃-based outer body for strength and cost control
-
Gradual transition layers to reduce thermal stress
Composite designs balance performance and economic efficiency.
4. Structural Design Optimization
4.1 Bore Geometry Optimization
The internal bore design has a decisive influence on nozzle life.
Recommended approaches:
-
Smooth, streamlined bore profiles
-
Optimized entry and exit angles to reduce turbulence
-
Avoid sharp corners and sudden cross-section changes
These measures minimize erosion and inclusion deposition.
4.2 Enlarged Working Layer Thickness
Increasing the thickness of the ZrO₂ working layer at high-wear zones significantly extends service life, especially for long sequence casting.
4.3 Sleeve-Type and Composite Bore Structures
Advanced designs include:
-
Sleeve-type bore inserts with ultra-high ZrO₂ content
-
Replaceable bore sleeves
-
Direct composite casting of different materials
These designs localize wear and delay catastrophic failure.
5. Manufacturing Process Control
5.1 Fine Powder Processing and Homogeneous Mixing
Uniform microstructure is critical. Key controls include:
-
High-energy mixing or co-milling
-
Narrow particle size distribution
-
Uniform stabilizer dispersion
Poor mixing leads to weak zones prone to corrosion and cracking.
5.2 High-Pressure Forming
Isostatic pressing or high-pressure uniaxial pressing:
-
Increases green density
-
Reduces open porosity
-
Improves mechanical strength
Dense microstructures resist slag penetration and erosion.
5.3 Optimized Sintering Regime
Sintering temperature and holding time must be precisely controlled:
-
Insufficient sintering leads to high porosity
-
Over-sintering causes grain coarsening and thermal shock sensitivity
Controlled sintering ensures optimal density and microstructural stability.
6. Anti-Clogging Technology
6.1 Low-Wettability Surface Design
Reducing steel and inclusion adhesion is essential.
Methods include:
-
High ZrO₂ content
-
Addition of anti-wetting phases
-
Surface densification treatment
6.2 Calcium Treatment Compatibility
Proper coordination between steel calcium treatment and nozzle material prevents excessive Al₂O₃ buildup.
Refractory composition must match steel chemistry to avoid adverse reactions.
6.3 Inert Gas Purging Optimization
Argon purging through the nozzle:
-
Suppresses inclusion deposition
-
Stabilizes flow
-
Reduces reoxidation
However, excessive gas flow can increase erosion and turbulence. Precise control is critical.
7. Tundish Operation and Process Control
7.1 Proper Preheating Practice
Uniform and sufficient preheating:
-
Eliminates moisture
-
Reduces thermal shock
-
Improves initial casting stability
Rapid or uneven heating is a common cause of early cracking.
7.2 Stable Casting Conditions
Avoiding abrupt changes in:
-
Casting speed
-
Steel temperature
-
Argon flow rate
Stable conditions significantly reduce thermal and mechanical stress on the nozzle.
7.3 Slag Management
Maintaining appropriate tundish slag composition and thickness:
-
Protects nozzle surface
-
Reduces oxidation
-
Minimizes chemical attack
Low-reactivity, low-FeO slags are preferred.
8. Quality Control and On-Site Management
8.1 Incoming Inspection of Nozzles
Key parameters to inspect:
-
Chemical composition
-
Bulk density and porosity
-
Bore geometry accuracy
-
Surface defects
Strict inspection prevents hidden quality risks.
8.2 Installation Accuracy
Proper alignment and sealing:
-
Prevent steel leakage
-
Avoid mechanical stress concentration
-
Ensure uniform wear
Installation procedures should be standardized and operator-trained.
8.3 Post-Use Analysis and Feedback
Analyzing used nozzles provides valuable insights:
-
Wear pattern analysis
-
Corrosion depth measurement
-
Clogging morphology observation
Feedback supports continuous product optimization.
9. Future Development Trends
Future improvements in tundish metering nozzle life will focus on:
-
Nano-structured and ultra-dense zirconia materials
-
Functionally graded materials (FGM)
-
Smart nozzles with real-time wear monitoring
-
Customized nozzle designs for specific steel grades
Integration of material science, fluid dynamics, and digital control will further enhance nozzle performance.
10. Conclusion
Improving the service life of tundish metering nozzles is a multidisciplinary engineering challenge involving refractory materials, structural design, manufacturing technology, steelmaking process control, and operational discipline. By systematically addressing corrosion, erosion, clogging, thermal shock, and mechanical damage, steel plants can significantly extend nozzle life, stabilize casting operations, and reduce production costs.
In practice, the most effective approach is not a single technical measure, but an integrated solution combining high-quality refractory materials, optimized nozzle design, precise manufacturing, compatible steel chemistry, and disciplined tundish operation. Continuous collaboration between steelmakers and refractory suppliers is essential to achieve long-term, sustainable performance improvements.
Tips You Shuold Know About The Tundish Metering Nozzle
Introduction To The Fast Change Mechanism Of Tundish Metering Nozzle
. Tundish Metering Nozzle&Zirconia Inserts
What Is The Composition Of Sub Entry Nozzle(SEN)
Ladle Shroud Gasket – Material, Function, Shape & Installation Guide
How to Use the Ladle Shroud Manipulator in Continuous Casting Operations
Operation procedure of dry material for induction furnace
Drawing design method and skill of ladle slide gate plate
slide gate plate test report In AK Middletown 225-ton ladle
Recycling slide gate plates to save costs and reduce waste