1. Introduction

In modern steelmaking, achieving consistent casting quality, reduced reoxidation, minimized molten steel splashing, and stable flow control are priorities for both cost efficiency and product quality. The ladle shroud plays a critical role in achieving these objectives. As a functional refractory component installed between the ladle and tundish, the ladle shroud ensures the controlled, protected, and turbulence-reduced transfer of molten steel.

While the design and material composition of ladle shrouds—typically alumina-carbon, alumina-zirconia-carbon, or zirconia-based—are vital to performance, the correct usage, handling, installation, and operational coordination also determine service life and casting quality outcomes. Improper usage of the ladle shroud may result in reoxidation inclusions, clogging, steel level fluctuations, or even catastrophic failures.

This article offers a comprehensive and systematic guide on how to use the ladle shroud effectively in the continuous casting process. It includes pre-operation preparation, installation, sealing methods, alignment, casting operation considerations, maintenance, safety precautions, and common troubleshooting.

---

2. Understanding the Function of the Ladle Shroud

Before learning to use the ladle shroud, it is essential to understand its operational purpose.

The ladle shroud functions to:

• shield molten steel from atmospheric oxygen during transfer

• prevent nitrogen pickup and steel reoxidation

• minimize turbulence and splashing

• maintain laminar flow conditions

• connect ladle nozzle and tundish safely

• protect molten steel purity and reduce inclusions

• reduce thermal losses and steel temperature drop

• prevent slag entrapment

In essence, correct ladle shroud application ensures cleaner steel, higher casting quality, and reduced refractory wear.

---

3. Preparations Before Using the Ladle Shroud

3.1 Inspection and Quality Verification

Before installation:

• verify shroud integrity (no cracks, chips, or internal defects)

• confirm dimensional tolerances

• inspect seating surfaces

• check for contamination

• verify anti-oxidation or coating layers

Dimensional accuracy and surface finishing are critical for sealing and flow stability.

3.2 Preheating and Conditioning

Depending on refractory material and steel plant practice:

• some shrouds require controlled pre-heating

• others are designed for cold installation

Improper thermal handling can cause:

• thermal shock

• cracking

• spalling

The use of warming chambers or ladle turret heating systems may be required.

3.3 Preparation of Ancillary Components

Before installation, ensure readiness of:

• connection flange

• shroud holder

• sealing gasket or refractory paste

• safety locking pins

• alignment fixtures

The sealing interface is particularly critical.

---

4. Installation of the Ladle Shroud

4.1 Correct Mounting Procedure

The shroud is typically mounted under the ladle nozzle, requiring:

• lifting tools (mechanical clamps, cranes)

• edge protection to avoid chipping

• secure alignment jigs

Ensure that the connection surface between shroud and ladle nozzle is:

• clean and dust-free

• free of slag or refractory debris

• level and flush

4.2 Sealing

The sealing method is crucial to avoid oxygen ingress:

• refractory gaskets (ceramic fiber, calcium silicate)

• refractory paste

• metallic clamps

• mechanical compression systems

Gasket thickness should be consistent to maintain sealing and avoid steel leakage.

4.3 Alignment

Proper alignment ensures:

• smooth nozzle flow

• reduced turbulence in tundish

• avoidance of collisions with tundish impact pad

• uniform casting stream

Laser or mechanical alignment tools may be used to position the shroud vertically.

4.4 Safety Locking

Safety devices are used to prevent:

• accidental disconnection

• movement during casting

• mechanical vibrations

Locking pins must be positioned securely.

---

5. Immersion and Connection with the Tundish

5.1 Immersion Technique

Correct immersion technique minimizes:

• thermal shock

• slag entrapment

• splashing

Best practices include:

• entering tundish through slag-free area

• avoiding impact pad collision

• controlled descending speed

5.2 Maintaining Immersion Depth

The ladle shroud tip should remain submerged:

• below the tundish slag-metal interface

• above the tundish bottom impact pad

Typical immersion depth ranges from 80 to 200 mm, depending on design and tundish steel height.

Incorrect depth results in:

• reoxidation (if too shallow)

• excessive turbulence (if too deep)

• slag entrapment (surface touching slag)

---

6. Operational Considerations During Casting

6.1 Controlling Flow Rate and Start-Up

At casting start:

• open nozzle gradually

• allow the shroud to stabilize

• monitor stream behavior

6.2 Avoiding Turbulence

Laminar flow is critical for:

• reduced inclusion entrapment

• lower refractory erosion

• improved steel cleanliness

Turbulence arises from:

• misaligned shroud

• excessive casting speed

• poor immersion depth

6.3 Avoiding Oxygen Aspiration

Key factors:

• sealing integrity

• immersion depth

• steady stream

• minimal vibration

Oxygen ingress leads to:

• oxide inclusions

• nozzle clogging

• steel quality loss

6.4 Coordination with Other Functional Refractories

The ladle shroud interacts with:

• ladle slide gate plate

• tundish impact pad

• SEN (sub entry nozzle)

• tundish argon purging systems

Proper coordination ensures balanced flow and reduced clogging.

---

7. Maintenance and Inspection During Casting

Operators must monitor:

• shroud position stability

• leakage

• slag entrainment

• nozzle clogging symptoms

• steel splash occurrence

• stream shape and continuity

Corrective actions may include:

• flow rate adjustment

• argon purging increase

• tundish level control

• stream protection checks

---

8. End of Heat and Removal Procedure

When casting ends:

• close ladle slide gate fully

• allow stream to stop

• lift shroud carefully using lifting clamps

• avoid rapid thermal shock during removal

After removal:

• inspect the shroud for wear patterns

• evaluate erosion zones

• document operational data for troubleshooting

---

9. Common Problems and Troubleshooting

9.1 Oxygen Aspiration

Cause:

• poor sealing

• shallow immersion

• cracked shroud

Solution:

• improved sealing gaskets

• immersion control

• pre-inspection

9.2 Slag Entrapment

Cause:

• immersion too deep or misplaced

• slag layer disturbance

Solution:

• adjust depth

• avoid slag touching

9.3 Nozzle Clogging

Causes:

• inclusion buildup

• reoxidation

• inadequate argon purging

Solutions:

• optimized steel composition

• consistent argon flow

9.4 Shroud Cracking or Spalling

Cause:

• thermal shock

• mechanical impact

• abrasive wear

Solution:

• proper pre-heating

• careful handling

---

10. Safety Considerations

Working with the ladle shroud involves molten steel and high temperature. Safety requirements include:

• heat-resistant PPE

• slag splash shields

• fire protection systems

• remote manipulation equipment

• emergency disengagement mechanisms

Operator training is essential.

---

11. Factors Influencing Shroud Performance

Performance depends on:

• refractory quality

• zirconia or spinel content

• carbon and antioxidant systems

• surface finish

• nozzle geometry

• gasket design

• tundish steel level

• casting speed

Higher-quality ladle shrouds often include:

• isostatic pressing

• zirconia reinforcement

• optimized pore distribution

---

12. Best Practices Summary

For optimal use:

• inspect before installation

• pre-heat when required

• apply proper sealing

• align accurately

• immerse steadily

• maintain correct depth

• monitor flow conditions

• coordinate with SEN and tundish

• ensure operator training

Correct usage leads to:

• cleaner steel

• longer sequence casting

• reduced inclusions

• stable flow

• improved tundish life

• lower refractory consumption

---

13. Conclusion

The ladle shroud is a critical part of the continuous casting system, and proper usage is essential for stable steel flow, reduced reoxidation, minimized slag entrainment, and enhanced steel cleanliness. While material design and manufacturing quality determine baseline performance, the correct application—installation, sealing, immersion, monitoring, and removal—controls real-world results.

Effective use of the ladle shroud directly impacts casting quality, production efficiency, and operational costs. Therefore, steel plants must invest not only in high-quality ladle shrouds but also in operator training, maintenance protocols, and systematic process control.

Mastering ladle shroud usage is a fundamental step toward achieving clean steel production and competitive continuous casting operations.

. Tundish Metering Nozzle&Zirconia Inserts

What Is The Composition Of Sub Entry Nozzle(SEN)

Ladle Shroud Gasket – Material, Function, Shape & Installation Guide

How to Use the Ladle Shroud Manipulator in Continuous Casting Operations

Refractory shapes and sizes

Operation procedure of dry material for induction furnace

Drawing design method and skill of ladle slide gate plate

slide gate plate test report In AK Middletown 225-ton ladle

Recycling slide gate plates to save costs and reduce waste

The top 5 ladle shroud manufacturers in China

The Role of Slide Gate Plates in Steel Industry Efficiency: Exploring the Mechanisms of LS, CS, and LG Series for Optimal Performance

The difference between magnesia carbon brick and aluminum magnesia carbon brick

Production and application of isostatically pressed refractory materials

New generation ladle slide gate system for performance improvement

Thermal Stress Cracking Of Ladle Slide Gate Plate

The-damage-reasons-to-ladle-sliding-plates-and-the-advantages-and-disadvantages-of-some-slide-gate-plates

The Unseen Champion Of Continuous Steel Casting-Slide Gate

5 Key Factors Behind Ladle Shroud Cracking

How To Extend The Service Life Of Slide Gate Plates In Steel Casting - Henan Yangyu Refractories Co.,Ltd

How To Choose Ladle Shroud From A China Factory

A Few Things You Should Know About The Ladle Nozzle

Wear Reason About The Slide Gate Plate

Before Enquiry Some Questions You Should Know About Ladle Shroud - Henan Yangyu Refractories Co.,Ltd

The Iso Refractory Trial Report Compared With Vesuvius

The drawing regarding kinds of slide gate plate

Slide Gate Plate Price Guide 2025: Complete Pricing Analysis and Buying Tips

Complete Guide to Submerged Entry Nozzle (SEN) in Steel Making

What Is A Ladle Shroud And Its Function - Henan Yangyu Refractories Co.,Ltd

How To Improve The Lifespan Of Slide Gate Plates

The Reason Of Sub Entry Nozzle Clogging And How To Slove It

Why The Tundish Stopper Cracks And How To Improve It

How To Avoid The Sub Entry Nozzle(SEN) Clogging